Maraging Steel

Steels

StrongChemical resistantFunctionalImpact resistant

Maraging steels form a class of iron alloys. This group of materials has a martensitic crystal structure and is strengthened via aging at approximately 500 °C (900 °F), hence the portmanteau "maraging". These ultra-low carbon alloys have very high strength and hardness properties derived from precipitation of intermetallic compounds rather than carbon content. It is a material best used for tooling inserts and molds. This alloy is also called X3NiCoMoTi 18-9-5 or 1.2709.

Print with Maraging Steel

Mechanical Properties

Tensile strength1000–1250 MPa

Tensile modulus135000–185000 MPa

Elongation8–15 %

Flexural modulus190000–210000 MPa

Density8 g/cm³

Print Constraints

Maximum build volume

420 × 420 × 450 mm

Default layer height0.05 mm

Default infill100%

Min embossing0.5 mm

Min engraving0.5 mm

Accuracy± 0.2 mm

Warping riskOver_140_mm

Interlocking partsSupported

Available finishes

Each finish can be combined with the available colors at checkout.

Sandblasted Matte

1 color

Sandblasted matte gray surface.

Satin Glossy

1 color

Glassblasted glossy gray surface.

All materials

Maraging Steel

Steels

StrongChemical resistantFunctionalImpact resistant

Print with Maraging Steel

Mechanical Properties

Tensile strength1000–1250 MPa

Tensile modulus135000–185000 MPa

Elongation8–15 %

Flexural modulus190000–210000 MPa

Density8 g/cm³

Print Constraints

Maximum build volume

420 × 420 × 450 mm

Default layer height0.05 mm

Default infill100%

Min embossing0.5 mm

Min engraving0.5 mm

Accuracy± 0.2 mm

Warping riskOver_140_mm

Interlocking partsSupported

Available finishes

Each finish can be combined with the available colors at checkout.

Sandblasted Matte

1 color

Sandblasted matte gray surface.

Satin Glossy

1 color

Glassblasted glossy gray surface.

All materials