Glass Fiber PEEK

Composites

Wear resistantHeat resistantChemical resistantUV resistant

Glass fiber PEEK provides improved creep strength and dimensional stability along with a high level of mechanical strength and rigidity. It offers outstanding resistance to a broad range of chemicals, including automotive fluids, is insoluble in all common solvents, and is Inherently flame resistant. These properties make this material suitable for use in parts which are exposed to high static loads over long periods in high temperature conditions. It is less suitable for bearing or wear applications.

Print with Glass Fiber PEEK

Mechanical Properties

Tensile strength105–160 MPa

Tensile modulus7250–9000 MPa

Elongation2.4–2.5 %

Flexural strength130–250 MPa

Flexural modulus5748–8500 MPa

Density1.44 g/cm³

Print Constraints

Maximum build volume

350 × 350 × 450 mm

Default layer height0.2 mm

Default infill20%

Min embossing0.5 mm

Min engraving0.5 mm

Accuracy± 0.3 mm

Warping riskHigh

Interlocking partsSupported

Available finishes

Each finish can be combined with the available colors at checkout.

Standard

1 color

Standard layered finish.

Sanded

1 color

Smooth sanded finish.

All materials

Glass Fiber PEEK

Composites

Wear resistantHeat resistantChemical resistantUV resistant

Print with Glass Fiber PEEK

Mechanical Properties

Tensile strength105–160 MPa

Tensile modulus7250–9000 MPa

Elongation2.4–2.5 %

Flexural strength130–250 MPa

Flexural modulus5748–8500 MPa

Density1.44 g/cm³

Print Constraints

Maximum build volume

350 × 350 × 450 mm

Default layer height0.2 mm

Default infill20%

Min embossing0.5 mm

Min engraving0.5 mm

Accuracy± 0.3 mm

Warping riskHigh

Interlocking partsSupported

Available finishes

Each finish can be combined with the available colors at checkout.

Standard

1 color

Standard layered finish.

Sanded

1 color

Smooth sanded finish.

All materials